Development of 17-4 PH Stainless Steel for Low-Power Selective Laser Sintering

Selective laser sintering (SLS) is one of the prominent methods of polymer additive manufacturing (AM). A low-power laser source is used to directly melt and sinter polymer material into the desired shape. This study focuses on the utilization of the low-power laser SLS system to successfully manufacture metallic components through the development of a metal-polymer composite material. In this study, 17-4 PH stainless powders are used and mixed with polyoxymethylene (POM) and high-density polyethylene (HDPE) to prepare the composite powder material. The polymeric mixture is removed during the thermal degreasing process and subsequent sintering results in a solid metallic component. Sinterit Lisa with a 5 W, 808 nm laser source is used to fabricate the green part. For the printing parameters of 140 °C, laser power of 35.87 mJ/mm², and layer thickness of 100 μm, the printed samples achieved a maximum density of 3.61 g/cm³ and a complete shape. After sintering at 1310 °C for 180 min, the tensile strength of the shrunk sample is 605.64 MPa, the hardness is HRC 14.8, the average shrinkage rate is 22%, and the density is 7.57 g/cm³, which can reach 97% of the theoretical density. This process allows the use of a wide range of particle sizes that the usual AM technologies have, making it a low-cost, low-energy-consumption, high-speed AM technology.