Comparative In vitro Analysis of Push-Out Bond Strength of Different Root Canal Sealers to Root Dentin
Joyeta Ghosh1, Bhagyesh J Cheta2, Yogesh V Rathod3
1Department of Pediatric and Preventive Dentistry, Kalinga Institute of Dental Sciences, KIIT Deemed to be University, Bhubaneswar, Odisha, India.
Aim:
The study's objective is to assess the bond strengths of four different endodontic sealers to root dentin using a push-out test technique.
Material And Method:
Sixty single-rooted teeth were selected and decoronated. Canal instrumentation was done using rotary files and divided into four groups (n = 15) based on the sealer used. Group 1: zinc oxide eugenol (ZOE)-based, Group 2: epoxy resin-based, Group 3: methacrylate-based, and Group 4: bioceramic. Following obturation with Gutta Percha, each tooth was prepared with root portions that were 2 mm thick at the apical and middle 1/3 so that universal testing equipment could measure the push-out bond strength. Tukey's post hoc tests and one-way ANOVA were used to examine the data.
Result:
According to the results, group 4 had the strongest push-out relationship, followed by groups 3, 2, and 1, respectively. It can be concluded that the bioceramic sealers have superior bond strengths.
Conclusion:
Bioceramic sealers demonstrated the highest bond strengths to root dentin, outperforming methacrylate, epoxy resin, and zinc oxide eugenol sealers in the push-out test.