Effect of Interfacial Compatibility on Mechanical Property of Polyamide 6 Modified by Polyborosiloxane

The interfacial properties of blends play a crucial role in determining the mechanical characteristics of polyamide alloys. This study focused on the preparation of PA6/PBS alloys via a melt blending method, utilizing 3-aminopropyltriethoxysilane (KH550) as the compatibilizer to examine the impact of KH550 on the interfacial and mechanical properties of these binary blends. The results demonstrated that the amino groups in KH550 reacted with the terminal carboxyl groups in polyamide 6 (PA6) and the B-OH in polyborosiloxane (PBS), which significantly enhanced interfacial adhesion between the two phases. A reduction in the particle size and interparticle distance of PBS particles was related to increased interfacial adhesion within the blends. The superior dispersion and robust interfacial adhesion caused a notable improvement in the notched Izod impact strength, rising from 7.9 kJ/m² to 29.7 kJ/m² at 25 °C and from 6.3 kJ/m² to 16.6 kJ/m² at -50 °C. Consequently, KH550 proved to be an effective toughening agent for the PA6/PBS system. Furthermore, the PA6/PBS blends containing a high content of KH550 induced a morphological transformation from a "sea-island" structure to a partially interpenetrating polymer network, leading to the absence of a double-yield phenomenon in the tensile curve.