The Effects of Cu Powder on the Interface Microstructure Evolution of Hot-Rolled Al 6061/Mg M21/Al 6061 Composite...

This study achieved the successful creation of a 6061/M21/6061 composite sheet, with Cu powder incorporated in the middle, through a two-pass hot roll bonding process. The effect of Cu powder addition on interface microstructure evolution of Mg-Al composite plate during annealing was studied. The results show that the incorporation of copper powder significantly suppresses the formation of Mg-Al intermetallic compounds (IMCs) at the boundary of Al-Mg bonded plates. The IMCs' thickness of composite plate Mg-Al interface absent Cu powder increased from 7.0 µm at 250 °C to 61.2 µm at 400 °C, showing a rapid growth trend. On the contrary, in the area with Cu powder of composite plate containing Cu powder, when the temperature ranges from 250 °C to 350 °C, the Mg-Al diffusion layer is thin and only varies between 1 µm and 3.2 µm and, even when the temperature rises to 400 °C, the diffusion layer is only 18.8 µm. At a constant temperature, the diffusion rate of IMCs in the Cu powder-containing region of the composite plate is significantly lower than that in the region without Cu powder. Upon the addition of Cu powder, Al₂Cu and Al_0.92Cu_1.08Mg phases are formed, which decrease the proportion of the brittle phases Al₃Mg₂ and Mg₁₇Al₁₂ at the composite plate interface, thereby effectively mitigating the diffusion of IMCs within the Mg-Al interface. This presents a novel concept for the investigation of enhanced interface bonding and the fabrication of Mg-Al composite plates.