Effect of Initial Rolling Temperature on the Microstructure Evolution of Liquified Nature Gas...

In order to gain insight into the changes of the organization and hardness of 500 MPa steel-grade low-temperature-resistant steel bars (HRB500DW) for liquefied nature gas (LNG) storage tanks during the continuous cooling phase transformation process, the effects of different rolling temperatures and cooling speeds on the organization of the phase change law, microstructure and hardness were studied. The results show that the critical phase transformation points A_C1 and A_C3 of the test steel were 702 and 880 °C, respectively. The organization of the test steel was polygonal ferrite and pearlite when the cooling rate was 1-2 °C/s. At a cooling speed of 5 °C/s, a small amount of bainite started to be produced in the region of a large deformation of rolling, and at 15 °C/s, some slate martensite started to be produced. At a cooling speed of 10 to 25 °C/s, the organization was mainly bainite. At a cooling rate of 40 °C/s, continuous pre-eutectic reticulated ferrite was formed at the austenite grain boundaries, reducing material properties. As the cooling speed increased, the hardness of the matrix organization of the test bars increased. The lower initial rolling temperature led to the expansion of the martensitic transformation zone. For rebar producers, the initial rolling temperature of 1050 °C was better than the initial rolling temperature of 1000 °C.