Effect of Bayer Red Mud on the Mechanical Strength of Grouting Material

The massive stockpiles of Bayer-process red mud (BRM) severely compromise soil integrity, necessitating the urgent development of efficient large-scale utilization strategies. BRM contains large amounts of calcium, silicon, and aluminum. Theoretically, water glass and flue gas desulfurization gypsum (FGD) can increase the active substances in BRM, making it a cementitious raw material capable of replacing cement. This study pioneers a novel activation strategy utilizing water glass-FGD synergism to amplify the BRM reactivity, enabling an increased dosage in construction materials through enhanced pozzolanic activity. They were blended into the cement at different ratios to prepare a grouting material (BF-C) for fissure sealing in mine rock strata. The hydration mechanism of BF-C was analyzed from a micro perspective by XRD, FTIR, ICP-OES, and SEM-EDS, and combined with the Ca/(Si + Al) ratio to reveal its hydration synergy. The results showed that the 3 d and 28 d strength of 70% BRM-FGD reached 8.94 MPa and 13.71 MPa, respectively. At this ratio, the hydration synergy of BF-C was the strongest. The addition of water glass and FGD can directly modulate the Ca/(Si + Al) ratio of the system to an optimal value of 0.94, which promotes the formation of early hydration products. C-S-H gel, calcite, and C(N)-A-S-H are the main hydration products of BF-C. C-S-H gels are encapsulated on cancrinite, and their three-dimensional network structures are dense. Meanwhile, C(N)-A-S-H crystals are interspersed between C-S-H gels, making the structure more stable. This achievement introduces an innovative method for the large-scale utilization of Bayer red mud, providing an effective solution in grouting technology using solid waste as raw material.