Evolution of silicate coordination in architected amorphous and crystalline magnesium silicates during carbon
Xun Gao1, Prince Ochonma2, Divya Prasad1
1School of Civil and Environmental Engineering, Cornell University, Ithaca, NY 14853, USA. gg464@cornell.edu.
Abstract:
Advancing durable solutions for carbon storage and removal at the gigaton scale to produce solid carbonates via carbon mineralization requires harnessing earth abundant magnesium silicate resources. Calibrated insights linking the structural and morphological features of earth abundant amorphous and crystalline magnesium silicate phases to their reactivity are essential for scalable deployment but remain underdeveloped. To resolve the influence of silica coordination and mass transfer on carbon mineralization behavior, magnesium silicates bearing amorphous and crystalline phases (AC Mg-silicate) are synthesized. The structural and morphological transitions starting from colloidal precursors to their final synthesized form on heating are delineated using operando ultra small/small/wide angle X-ray scattering (USAXS/SAXS/WAXS) measurements. The evolution of the silicate phases on carbon mineralization of AC Mg-silicate is contrasted with that of highly crystalline Mg-silicate (HC Mg-silicate) when reacted at 200 °C and a CO2 partial pressure of 20 atm in water and 1 M NaHCO3 solution in stirred and unstirred environments. These experimental conditions are analogous to those of the water-gas-shift reaction for sustainable recovery of H2 with inherent carbon mineralization. Enhancement in the extent of carbon mineralization by 13.3-19.5% noted in the presence of NaHCO3 compared to water in AC and HC Mg-silicate with and without stirring, is attributed to the buffering effect which aids simultaneous silicate dissolution and carbon mineralization. Enhanced extents of carbon mineralization in the presence of NaHCO3 correspond to the formation of MgSiO3 and SiO2 phases from the starting Mg2SiO4 precursors in AC and HC Mg-silicate. Unlocking these silicate transformations during carbon mineralization by harnessing architected Mg-silicate precursors reveals the feasibility of integrating these chemical pathways with sustainable H2 conversion pathways with inherent carbon mineralization.
Related Concept Videos
02:42Ionic Crystal Structures
Most monatomic ions behave as charged spheres, and their attraction for ions of opposite charge is the same in every direction. Consequently, stable structures for ionic compounds result (1) when ions of one charge are surrounded by as many ions as possible of the opposite...
01:24Hydration of Cement
02:34Structural Isomerism
Isomers are different chemical species that have the same chemical formula. Structural isomerism of coordination compounds can be divided into two subcategories, the linkage isomers and coordination-sphere isomers.
Linkage isomers occur when the coordination compound contains a ligand that can bind to the transition metal center through two different atoms. For example, the CN− ligand can bind through the carbon atom or through the nitrogen atom. Similarly, SCN− can...
02:46Crystal Field Theory - Tetrahedral and Square Planar Complexes
Crystal field theory (CFT) is applicable to molecules in geometries other than octahedral. In octahedral complexes, the lobes of the dx2−y2 and dz2 orbitals point directly at the ligands. For tetrahedral complexes, the d orbitals remain in place, but with only four ligands located between the axes. None of the orbitals points directly at the tetrahedral ligands. However, the dx2−y2 and dz2 orbitals (along the Cartesian axes) overlap with the ligands less than the dxy,...
01:23Properties of Organometallic Compounds
01:26Alkali Aggregate Reaction in Concrete