Study on the failure of oil-contaminated wheel-rail conditions

Zhou Gaowei1,2, Zhou Jiajun3, Tian Chun3

  • 1Engineering Research Center of Continuous Extrusion, Ministry of Education, Dalian Jiaotong University, Dalian, China.

Plos One
|March 12, 2025
PubMed

More Related Videos

Determining Tribocorrosion Rate and Wear-Corrosion Synergy of Bulk and Thin Film Aluminum Alloys07:12

Determining Tribocorrosion Rate and Wear-Corrosion Synergy of Bulk and Thin Film Aluminum Alloys

Published on: September 11, 2018

11.2K
Failure of Cleaning Verification in Pharmaceutical Industry Due to Uncleanliness of Stainless Steel Surface07:00

Failure of Cleaning Verification in Pharmaceutical Industry Due to Uncleanliness of Stainless Steel Surface

Published on: August 11, 2017

8.1K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
169
Rolling Resistance01:21

Rolling Resistance

When a solid cylinder rolls steadily on a rigid surface, the normal force applied by the surface on the cylinder is perpendicular to the tangent at the contact point. However, since no materials are entirely rigid, the surface's reaction to the cylinder involves a range of normal pressures.
For instance, imagine a hard cylinder rolling on a comparatively soft surface. The cylinder's weight compresses the surface beneath it. As the cylinder moves, the material in front of it slows down...
248
Residual Stresses01:26

Residual Stresses

Residual stresses reside in a structure even after removing the original stress inducer. This phenomenon often arises from varied plastic deformations across different parts of a structure. Consider a rod stretched beyond its yield point. It will not regain its original length due to permanent deformation. Even after load removal, the rod does not entirely lose stress because of uneven plastic deformations, resulting in residual stresses. The computation of these stresses in structures is...
198
Rolling Resistance: Problem Solving01:17

Rolling Resistance: Problem Solving

Rolling resistance, also known as rolling friction, is the force that resists the motion of a rolling object, such as a wheel, tire, or ball, when it moves over a surface. It is caused by the deformation of the object and the surface in contact with each other, as well as other factors like internal friction, hysteresis, and energy losses within the materials. Rolling resistance opposes the object's motion, requiring additional energy to overcome it and maintain movement. In practical...
277
Friction: Problem Solving01:21

Friction: Problem Solving

Friction is an essential force that influences the motion of objects in daily life. Depending on the situation, it can be either beneficial or problematic. Consider a bus with a mass of three megagrams and its center of mass at a specific point, moving along a banked road at a constant speed. The coefficient of static friction between the tires and the road is 0.5. Find the maximum angle of the banked road at which the bus would not slip or tip.
Initially, a visual representation of the...
193
Dry Friction01:30

Dry Friction

Dry friction occurs between two solid surfaces in contact as they attempt to move relative to one another. In daily life, dry friction is encountered in various forms, such as when walking on the ground, sliding an object across a table, or rubbing hands together. Despite its ubiquity, the underlying mechanisms behind dry friction are not readily visible.
To illustrate this concept, imagine a wooden crate resting on a rough, non-uniform horizontal surface. When an external force is applied to...
325