Development and Evaluation of a Polymer Composite Material Reinforced by Tectona Grandis Fiber, with Static Analysis

This research seeks to investigate the viability of using Tectona grandis wood powder as a reinforcement material in polymer matrix composites because of the increasing awareness of natural fibers that offer impressive characteristics and cost-effectiveness in addition to being biodegradable. The fibers were mixed with epoxy resin, and the mixture was passed through a filter to remove fiber bundles and then compression molded to form composites, which were cured in an oven. Different experiments were performed on the composite to measure its mechanical characteristics. The tests performed were a tensile test to measure the mechanical properties of the material like strength and elastic properties, a compression test for evaluating the behavior of the material under a compressive load, a hardness test for the rate of indentation resistivity, and an impact test for the material's ability to withstand shock loads. The results showed that fiber reinforcement caused a significant enhancement in the mechanical aspect of the composite, where the compression strength obtained was 249.83 MPa, and the tensile strength obtained was 17.98 MPa. SEM microstructural analysis and a moisture absorption test were performed, while an additional analysis was carried out using Ansys work bench software. This research proves that Tectona grandis wood powder improves the mechanical properties of polymer composites and represents a viable substitute for synthetic reinforcements.