Cavitation Erosion of Protective Coating Based on Cordierite Filler and Epoxy Matrix

Marko Pavlović1, Marina Dojčinović2, Jasmina Nikolić2

  • 1Innovation Centre of Faculty of Mechanical Engineering, University of Belgrade, 11000 Belgrade, Serbia.

Materials (Basel, Switzerland)
|March 13, 2025
PubMed

Keywords:
cavitation resistancecordierite fillermetal substratemicrostructure

More Related Videos

Experimental Multiscale Methodology for Predicting Material Fouling Resistance09:13

Experimental Multiscale Methodology for Predicting Material Fouling Resistance

1.4K
Fused Filament Fabrication FFF of Metal-Ceramic Components08:43

Fused Filament Fabrication FFF of Metal-Ceramic Components

Published on: January 11, 2019

17.1K

Related Concept Videos

Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
104
Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
89
Effect of Sea Water on Concrete01:22

Effect of Sea Water on Concrete

Concrete exposed to seawater can undergo degradation like the dissolution of ettringite and gypsum, increasing the material's porosity and decreasing its strength. In contrast, the crystallization of salts within the concrete's pores can cause expansion, particularly above the waterline where evaporation occurs. Nonetheless, this expansion only happens when seawater, enabled by the concrete's permeability, manages to infiltrate the structure.
Concrete in areas between tide marks,...
127
Mortar Joint Deterioration in Masonry01:13

Mortar Joint Deterioration in Masonry

Mortar joint deterioration is a significant concern in masonry structures, with water accumulation in the joints leading to damage from freeze-thaw cycles. The repeated expansion of water during freezing and its melting during thawing develop and propagate cracks in the masonry joints. Eventually, this leads to the spalling of mortar from the joints, loosening masonry units and weakening the structure. The deteriorated mortar joints are also vulnerable to moisture intrusion into the walls.
The...
101