Evaluation of Physical Changes and Bond Properties of Monolithic Zirconia Following Surface Treatment with Alumina and Synthetic Diamond Particles: A Comparative X-ray Diffraction Analysis
Arshi I Kazi1, Ramandeep Dugal2, Pallavi Madanshetty3
1Department of Prosthodontics, MA Rangoonwala College of Dental Sciences and Research Centre, Pune, Maharashtra, India, Orcid: https://orcid.org/0000-0001-5841-9283.
Aim:
The aim of this study was to compare and evaluate the phase transformation and effect on the bond strength and fracture toughness of monolithic zirconia after surface treatment with alumina and synthetic diamond particles.
Materials And Methods:
Forty samples of monolithic sintered zirconia discs (Y-TZP) were divided into two groups of 20 samples each. Group A - air abrasion with alumina particles (n = 20); group B - air abrasion with synthetic diamond particles (n = 20). Pretreatment phase and posttreatment of each zirconia sample from group A and group B were evaluated using an X-ray diffraction machine. The surface roughness of each zirconia sample was evaluated using a profilometer. Composite discs were fabricated and bonded to the air-abraded surface of each zirconia sample from group A and group B using a dual-cured resin cement, respectively. These samples were mounted in an acrylic block to determine the bond strength of zirconia with resin cement using a universal testing machine. This was followed by a fracture toughness test of the samples using a Vickers indentation hardness tester. The results were subjected to statistical analysis using a t-test, and relevant statistical conclusions were drawn.
Results:
The mean ± SD of monoclinic content in group A (alumina particles) and group B (synthetic diamond particles) was 0.82 ± 0.010% and 0.76 ± 0.015%, respectively. The mean ± SD of surface roughness in group A (alumina particles) and group B (synthetic diamond particles) was 0.507 ± 0.106 and 0.513 ± 0.116 µm, respectively, and the mean ± SD of bond strength in group A (alumina particles) and group B (synthetic diamond particles) was 6.11 ± 1.47 and 6.49 ± 0.83 MPa, respectively. The mean ± SD of fracture toughness in group A (alumina particles) and group B (synthetic diamond particles) was 2.63 ± 0.46 0.5 and 5.70 ± 1.03 MPam0.5, respectively. p < 0.05 was considered statistically significant.
Conclusion:
The distribution of mean monoclinic content was significantly higher in zirconia samples abraded by alumina (Group A) as compared to synthetic diamond particles (Group B). The mean surface roughness and bond strength results were statistically insignificant between both groups. The distribution of mean fracture toughness was significantly higher in group B compared to group A.
Clinical Significance:
Synthetic diamond particles for air abrasion of Y-TZP can be a promising alternative to alumina as they cause minimal changes in the structural integrity without compromising the bond strength. How to cite this article: Kazi AI, Dugal R, Madanshetty P, et al. Evaluation of Physical Changes and Bond Properties of Monolithic Zirconia Following Surface Treatment with Alumina and Synthetic Diamond Particles: A Comparative X-ray Diffraction Analysis. J Contemp Dent Pract 2024;25(12):1110-1117.
More Related Videos
10:36Stress Distribution During Cold Compression of Rocks and Mineral Aggregates Using Synchrotron-based X-Ray Diffraction
Published on: May 20, 2018
12:18Co-localizing Kelvin Probe Force Microscopy with Other Microscopies and Spectroscopies: Selected Applications in Corrosion Characterization of Alloys
Published on: June 27, 2022
Related Concept Videos
01:10X-ray Diffraction of Biological Samples
According to Bragg's law, when X-rays strike the sample positioned on a stage, the rays are scattered by the electron clouds around the sample atoms. The X-ray diffraction or scattering is caused by constructive interference of the X-ray waves that reflect off the internal crystal...
01:29Determination of Crystal Structures