Material Damage to Multielectrode Arrays after Electrolytic Lesioning is in the Noise

The quality of stable long-term recordings from chronically implanted electrode arrays is essential for experimental neuroscience and brain-computer interfaces. This work uses scanning electron microscopy (SEM) to image and analyze eight 96-channel Utah arrays previously implanted in motor cortical regions of four subjects (subject H = 2242 days implanted, F = 1875, U = 2680, C = 594), providing important contributions to a growing body of long-term implant research leveraging this imaging technology. Four of these arrays have been used in electrolytic lesioning experiments (H = 10 lesions, F = 1, U = 4, C = 1), a novel electrolytic perturbation technique using small direct currents. In addition to surveying physical damage, such as biological debris and material deterioration, this work also analyzes whether electrolytic lesioning created damage beyond what is typical for these arrays. Each electrode was scored in six damage categories, identified from the literature: abnormal debris, metal coating cracks, silicon tip breakage, parylene C delamination, parylene C cracks, and shank fracture. This analysis confirms previous results that observed damage on explanted arrays is more severe on the outer-edge electrodes versus inner electrodes. These findings also indicate that are no statistically significant differences between the damage observed on normal electrodes versus electrodes used for electrolytic lesioning. This work provides evidence that electrolytic lesioning does not significantly affect the quality of chronically implanted electrode arrays and can be a useful tool in understanding perturbations to neural systems. Finally, this work also includes the largest collection of single-electrode SEM images for previously implanted multielectrode Utah arrays, spanning eleven different intact arrays and one broken array. As the clinical relevance of chronically implanted electrodes with single-neuron resolution continues to grow, these images may be used to provide the foundation for a larger public database and inform further electrode design and analyses.