Regional Characteristics in Ultradeep MXene Slit Nanopores: Insights from Molecular Dynamics Simulation

The presence of slit nanopores in MXene materials inevitably influences the electrochemical performance of supercapacitor electrodes. However, most studies focus on experimental approaches, lacking microscopic-scale analysis. Here, we performed molecular dynamics (MD) simulations to thoroughly analyze and predict the ion transport pathways and energy storage mechanisms of MXene/ionic liquid (IL) supercapacitors with ultradeep slit nanopores. The simulation results indicate that during the charging process, counterions migrate from the bulk region into the electrode pores, forming a counterion layer near the electrode surface, while some co-ions gradually exit the pores. When charging is completed, a distinct ion layering structure emerges. As the interlayer spacing varies, the ion distribution in the electrode pores exhibits regional characteristics: in the ordered region near the bulk region, a stable electrical double-layer (EDL) structure is maintained, whereas in the deeper mixed region, persistent co-ion presence and significant disorder are observed. Dominated by the mixed region, the total energy variation of the electrode decreases as the interlayer spacing decreases, with energy changes of 8526.52, 7443.52, and 6640.99 kJ·mol^-1 at interlayer spacings of 1.2, 1.0, and 0.8 nm, respectively, representing reductions of approximately 12.7 and 22.1% compared to 1.2 nm. In the mixed region, after compensating for the interaction between counterions, the contribution of the interaction between counterions and electrode increases with decreasing interlayer spacing, reaching 123, 153, and 176% at 1.2, 1.0, and 0.8 nm, respectively. An increasing amount of energy is offset by interactions related to the co-ions, ultimately leading to the observed energy differences. These findings offer new insights into the impact of nanopore structure on supercapacitor performance and provide theoretical guidance for optimizing electrode design.