Structural, optical, and magnetic behavior and the nucleation of a Griffiths-like phase in (Ca,V)-doped ZnO...

Single-phase (Ca,V) co-doped ZnO nanoparticles (Zn_0.93Ca_0.04V_0.03O, called hereinafter ZCVO) were synthesized via a modified sol-gel method. The hexagonal wurtzite symmetry of the ZnO phase nanostructure, belonging to the P6₃mc space group, has been confirmed through X-ray diffraction examinations using Rietveld refinement. No segregated secondary phases or Ca or/and V-rich clusters were detected. The TEM images clearly show the presence of nanoparticles exhibiting a diverse range of spherical shapes. The effect of co-doping on the optical band gap and crystalline quality was also investigated via photoluminescence (PL), UV-vis, and Raman spectrometers. The M-T curve suggests a tenability of magnetic coupling which was discussed within the context of three competing magnetic phases using the 3D spin wave model and Curie-Weiss law. The lack of saturation of the M-H loop at 10 K suggests the presence of both paramagnetic (PM) and ferromagnetic (FM) phases in ZCVO NPs. The bound magnetic polaron (BMP) model provides a plausible explanation for the observed magnetic phase transition. Moreover, a Griffiths-like phase was observed for the first time, to our knowledge, in co-doped ZnO nanoparticles. This novelty may stem from the interplay between the antiferromagnetic (AFM) and FM interactions of the Ca and V ions, which are acquired by oxygen deficiency.