Preparation of Laminated Titanium Matrix Composites with High Strength and Plasticity via Regulating Heat Treatment...

In order to achieve a balance between the strength and ductility of titanium matrix composites (TMCs), a spray deposition method was employed to deposit carbon nanotubes (CNTs) onto the surface of Ti foil. Subsequently, spark plasma sintering (SPS) at 850 °C and an additional 1 h heat treatment at 880 °C were utilized to fabricate two laminated composites of different composition, namely, CNTs/Ti (SPS) and in situ TiC/Ti (SPS+HT). The microstructure evolution, mechanical properties, and strengthening and fracture mechanisms of laminated composites were systematically studied. The results revealed that after sintering at 850 °C, the reaction between CNTs and the titanium matrix was limited. However, after a 1 h heat treatment at 880 °C, CNTs were completely transformed into TiC, while the titanium matrix remained α phase without undergoing phase transformation. Through rolling and annealing, TiC particles were refined to 500 nm and exhibited a flattened shape. The in situ TiC/Ti layered composite material exhibited a tensile strength (UTS) of 491.51 MPa, which was a 29.63% improvement compared to pure titanium (379.16 MPa), and significantly higher than the UTS of CNTs/Ti samples (419.65 MPa). The primary strengthening mechanism was load transfer strengthening. The elongation (EL) remained at 26.59%, slightly lower than pure titanium (29.15%) and CNTs/Ti samples (27.51%). This can be attributed to the increased connectivity of the matrix achieved through rolling, which enhanced the ability to passivate cracks and prolonged the crack propagation path. This study presents a method for preparing laminated titanium matrix composites with both strength and ductility by controlling the heat treatment process.