Samarium-Promoted Layered La₂NiO₄ Perovskite for Hydrogen Production via the Auto-Thermal Reforming of Acetic Acid

The auto-thermal reforming (ATR) of acetic acid is an effective hydrogen production method, but it suffers from catalyst deactivation by coking. Sm-promoted layered La₂NiO₄ perovskite catalysts were synthesized via the sol-gel method and its catalytic performance in the ATR of HAc was further evaluated. The characterization results demonstrate that the incorporation of Sm into the lattice of La₂NiO₄ perovskite led to the formation of Ni-La-Sm-O species, inducing crystal defects in the perovskite structure which could promote the gasification of coking precursors. Additionally, Sm regulated the reduction characteristics of La₂NiO₄, resulting in the formation of highly dispersed nickel nanoparticles upon the hydrogen reduction, which increased the number of active sites available for acetic acid conversion. Consequently, a stable reactivity without obvious coking was obtained over a Ni_0.42La_0.7Sm_0.36O_2.01±δ catalyst within the ATR of Hac. The hydrogen yield reached 2.53 mol-H₂/mol-HAc along with the complete conversion of acetic acid.