Microstructure and Mechanical Properties of Nb₃₅Zr₂₆Ti₁₉Hf₁₅Mo₅ Refractory High-Entropy Alloy Under Rolling and Heat...

Refractory high-entropy alloys (RHEAs) have drawn much attention in the field of materials science for their unique properties and wide compositional design space. The Nb₃₅Zr₂₆Ti₁₉Hf₁₅Mo₅ alloy is important for exploring RHEAs' potential in high-temperature applications. It can break through existing material limitations and bring benefits to related fields, especially in the aerospace field. This paper focuses on Nb₃₅Zr₂₆Ti₁₉Hf₁₅Mo₅ RHEAs and studies the effects of cold rolling and heat treatment on its microstructure and mechanical properties. The alloy has a single-phase BCC structure. As rolling reduction rises from 20% to 80%, the alloy's strength increases notably while plasticity drops. At 80% rolling reduction, the tensile strength reaches 1408 MPa, and the elongation is 10.5%. During rolling, grains deform along the rolling direction, the number of low-angle grain boundaries grows, and dislocation and solid solution strengthening effects are enhanced. With the increase in annealing temperature, recrystallized grains increase, and the change in grain-boundary structure weakens the strengthening effect, leading to a strength decrease and a plasticity increase. After annealing at 800 °C, the elongation reaches 17%, and the dislocation density in the alloy decreases with a recrystallization degree of 49%.