Synthesis, Characterization, and Investigation of the Properties of a New Promising Poly(Azomethine) Organic...

A new poly(azomethine) with improved solubility was successfully prepared by the polycondensation of terephthalaldehyde and 2,2-Bis[4-(4-aminophenoxy)phenyl]-hexafluoropropane (4-BDAF) under green chemistry conditions. This new polymer containing hexafluoroisopropylidene was compared with a polymer containing isopropylidenediphenyl to study the influence of the presence of fluorine atoms on the properties of the polymer. Both were characterized by nuclear magnetic resonance (NMR), their molecular weight was measured by gel permeation chromatography (GPC), and their morphology was studied by X-ray diffraction (XRD). The two polymers obtained were soluble in most polar aprotic solvents and even in less polar solvents, which are practical and easily accessible solvents. Their thermal properties were determined by a thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). These two new polymers showed high resistance to thermal decomposition up to 490 °C, with a glass transition temperature (Tg) of 180 °C. The photophysical properties were studied by UV/Visible absorption. The polymers were doped and then deposited on cellulose filaments, an approach that made it possible to produce self-supporting conductive composites thanks to their mechanical properties. The topography of the resulting materials was characterized at submicron scales before estimating their electronic conductivity and gap energy by diffuse reflection spectroscopy.