A Study on the Corrosion Behavior of Fe/Ni-Based Structural Materials in Unpurified Molten Chloride Salt

The molten salt reactor is a fourth-generation nuclear power plant considered a long-term eco-friendly energy source with high efficiency and the potential for green hydrogen production. The selection of alloys for such reactors, which can operate for more than 30 years, is a primary concern because of corrosion by high-temperature molten salt. In this study, three Fe- and Ni-based alloys were selected as structural material candidates. Corrosion immersion tests were conducted in NaCl-KCl molten salt for 48 h at 800 °C and 40% RH conditions in an air environment. In the absence of moisture and oxygen removal, ClNaK salt-induced damage was observed in the investigated alloys. The corrosion behavior of the alloys was characterized using various techniques, including scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray photoelectron spectroscopy, and Auger electron spectroscopy. The results show that the corrosion process can be explained by salt-induced surface damage, internal ion migration, and depletion to the surface. The corrosion rate is high in SS316L (16Cr-Fe), N10003 (7Cr-Ni), and C-276 (16Cr-Ni), in decreasing order. Based on the corrosion penetration, ion elution, and interfacial diffusion results, C-276 and N10003 are good candidates for structural materials for MSRs. Therefore, Ni-based alloys with high Cr content minimize surface damage and ion depletion in unpurified molten salt environments. This indicates that Ni-based alloys with high Cr content exhibit highly corrosion resistance.