Study on the Preparation and Properties of Thermally Conductive Semi-Aromatic Heat-Resistant PA5T-CO-10T/ Hexagonal...

In this paper, we report a novel thermally conductive semi-aromatic heat-resistant PA5T-CO-10T/hexagonal boron nitride (PA5T-CO-10T/BN) composite, based on as-synthesized PA5T-CO-10T, which is a copolymer of poly (pentamethylene terephthalamide) (PA5T) and poly (decamethylene terephthalamide) (PA10T). We confirmed the structure of PA5T-CO-10T through a nuclear magnetic resonance carbon spectrometer (¹³C-NMR). The differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) results indicate that PA5T-CO-10T demonstrates a processing window (greater than 90 °C) which is suitable for melt processing and injection molding. Moreover, the PA5T-CO-10T composites with different BN contents were tested by scanning electron microscopy (SEM), a thermal conductivity meter, a rotational rheometer and X-ray diffraction (XRD). The results indicate that as the content of h-BN increases, the thermal conductivity of the PA5T-CO-10T/BN composites is significantly enhanced. When the mass of h-BN reaches 30 wt%, the thermal conductivity of the composite material is 2.5 times that of the original matrix resin. Simultaneously, there is a notable upward trend observed in the storage modulus, loss modulus, complex viscosity and orientation degree of h-BN. This is attributed to the high thermal conductivity and the high orientation degree of h-BN, which ensure the continuous enhancement of the material's thermal conductivity. Additionally, the introduction of h-BN enhances the degree of connection between the material's molecular chains. PA5T-CO-10T/BN possesses excellent heat resistance and thermal conductivity, presenting significant application prospects in the fields of electronics, electrical appliances and automobiles.