Research on the Thermal Aging Characteristics of Cured Epoxy Resin Insulating Materials for DC Bushings

High-temperature-resistant epoxy composites play a crucial role in enhancing the operational reliability and service life of devices such as DC bushings, which is of great significance for the long-term stable operation of ultra-high voltage and flexible power transmission and distribution systems. In this study, the epoxy composite was prepared, and long-term thermal aging tests were conducted at 250 °C and 270 °C. The changes in physical properties, electrical characteristics, and bending strength of epoxy composite were systematically investigated, and the thermal aging mechanism of these materials was elucidated. The experimental results revealed that with the progression of thermal aging, the epoxy composites exhibited volume shrinkage due to the breaking of chemical bonds. After 10 thermal aging cycles at 270 °C, the mass loss rate of the epoxy composite reached 20.52%. At 250 °C, the breakdown strength decreased by 9.9% compared to the unaged state. After aging at 250 °C and 270 °C, the volume resistivity decreased by a maximum of 53.75% and 76.94%, respectively, while the dielectric constant decreased by a maximum of 50.34% and 41.94%, respectively. After 10 aging cycles at 250 °C and 270 °C, the bending strength of the cured epoxy composite decreased by 39.79% and 53.91%, respectively. These findings provide valuable insights into the thermal aging characteristics of epoxy composites used in DC bushings and other electrical devices, offering a scientific basis for material selection and reliability assessment in high-voltage insulation applications.