Recrystallization Behavior of Cold-Rolled AA5083 Microalloyed with 0.1 wt.% Sc and 0.08 wt.% Zr

The influence of annealing temperature on the mechanical properties, microstructural evolution, and recrystallization behavior of AA5083 cold-rolled sheets with and without Sc/Zr microalloying was studied utilizing hardness tests, optical microscopy, electron backscatter diffraction, and transmission electron microscopy. The results show that a minor addition of Sc/Zr to the Al-Mg-Mn alloy can significantly improve the alloy strength and recrystallization resistance. Adding 0.1 wt.% Sc and 0.08 wt.% Zr raised the recrystallization temperature of heavily deformed sheets to 500 °C, which is 250 °C higher than for the Sc-free base alloy. The higher recrystallization resistance of the Sc-bearing alloy was mainly attributed to the presence of Al₃(Sc,Zr) nanoparticles, which enhanced the Zener drag pressure and delayed recrystallization. Grain boundary strengthening effects at various annealing temperatures were estimated using a constitutive equation. This work revealed that grain structure change and the corresponding boundary strengthening effect are key factors governing alloy strength evolution during annealing.