Microstructure and Wear Behavior of WMoTaNbV Refractory High-Entropy Alloy Coating on Ti6Al4V Alloy Surface Prepared...

WMoTaNbV refractory high-entropy alloys (RHEAs) have received widespread attention due to their excellent low-temperature toughness, hardness, and wear resistance. In recent years, the rapid development of surface modification technology represented by laser cladding has provided a new technological path for RHEA surface forming, and at the same time put forward higher requirements for raw material powder. In this study, WMoTaNbV RHEA spherical powder was prepared by radiofrequency plasma spheronization, and then WMoTaNbV RHEA coating was prepared on the surface of Ti6Al4V (TC4) alloy by laser cladding technique. The experimental results show that the prepared alloy powders have very high sphericity and are almost free of agglomeration and oxidation. Coatings with laser powers of 3.1-3.9 kW (gradient setting of 2 kW) were tested, with the 3.3, 3.5, and 3.7 kW coatings showing the best of the abrasion resistance. The microhardness of the 3.3 kW, 3.5 kW, and 3.7 kW coatings was 1.72, 1.97, and 1.76 times higher than that of the substrate, and the wear resistance was 1.83, 3.42, and 2.13 times higher than that of the TC4 substrate, respectively. This experimental result shows that the surface hardness and wear resistance of WNbMoTaV RHEA coating can be effectively improved by precisely regulating the laser power, thus improving the surface hardness and friction and wear properties of TC4 titanium alloy.