Process and Properties of Al-Mg-Er-Zr-Sc High-Strength Aluminum Alloy Powder Prepared by Vacuum Induction Melting Gas...

The Er-Zr-Sc-modified Al-Mg alloys produced by additive manufacturing (AM) exhibit good formability and excellent mechanical properties, and present great potential for applications in the fields of aerospace and automotive fields. In this work, the preparation process of Al-4.5Mg-0.7Er-0.5Zr-0.3Sc high-strength aluminum alloy powder for additive manufacturing by vacuum induction melting gas atomization (VIGA) was investigated. With the goal of obtaining excellent sphericity and higher powder yield in the particle size range of 15~53 μm, a new type atomizer with optimized convergence angle and tube extension length was designed based on finite element numerical simulation and experimental research, and the optimal atomization processing parameters were determined. The results revealed that when the convergence angle was 32° and the extension length was 5 mm, the large negative pressure and suction force at the tube outlet could facilitate the smooth flow of the melt and a refined powder particle size; when the melt temperature was 800 °C and the atomization pressure was 3.25 Mpa, the melt had low viscosity and the atomization gas could fully interact with the melt. Meanwhile, the melt droplets had suitable cooling conditions, avoiding the generation of irregular powders and improving the powder sphericity. Under the above optimal processing parameters, the prepared powders were spherical or nearly spherical with fine particle size and a high yield of about 39.45%.