Aspartame Endowed ZnO-Based Self-Healing Solid Electrolyte Interface Film for Long-Cycling and Wide-Temperature...

Metallic Zn anodes suffer from hydrogen evolution and dendritic deposition in aqueous electrolytes, resulting in low Coulombic efficiency and poor cyclic stability for aqueous Zn-ion batteries (AZIBs). Constructing stable solid electrolyte interphase (SEI) with strong affinity for Zn and exclusion of water corrosion of Zn metal anodes is a promising strategy to tackle these challenges. In this study, we develop a self-healing ZnO-based SEI film on the Zn electrode surface by employing an aspartame (APM) as a versatile electrolyte additive. The hydrophobic nature and strong Zn affinity of APM can facilitate the dynamic self-healing of ZnO-based SEI film during cyclic Zn plating/stripping process. Benefiting from the superior protection effect of self-healing ZnO-based SEI, the Zn║Cu cells possess an average coulombic efficiency more than 99.59% over 1,000 cycles even at a low current density of 1 mA cm^-2- 1 mAh cm^-2. Furthermore, the Zn║NH₄⁺-V₂O₅ full cells display a large specific capacity of 150 mAh g^-1 and high cyclic stability with a capacity retention of 77.8% after 1,750 cycles. In addition, the Zn║Zn cell delivers high temperature adaptability at a wide-temperature range from - 5 to 40 °C even under a high DOD of 85.2%. The enhanced capability and durability originate from the self-healing SEI formation enabled by multifunctional APM additives mediating both corrosion suppression and interfacial stabilization. This work presents an inspired and straightforward approach to promote a dendrite-free and wide-temperature rechargeable AZIBs energy storage system.