Effect of Laser Processing Parameters on the Quality of Titanium Alloy Cladding Layer on Carbon Fiber-Reinforced...

To address the insufficient bonding performance between TC4 (Ti-6Al-4V) coating and carbon fiber-reinforced thermoplastic (CFRP) matrices that limits engineering applications of composite structures, TC4 coatings were fabricated on CFRP polymer composites via laser cladding and analyzed using scanning electron microscopy (SEM) and transmission electron microscopy (TEM) to examine the interface morphology, microstructure, and phase composition. The influence of laser processing parameters on the cladding quality was assessed based on the mechanical performance of the TC4 coating. The findings revealed that insufficient laser power (<230 W) or excessive scanning speed (>1.4 m/min) led to incomplete melting of TC4 powder, preventing the formation of intermetallic compound (IMC) layers. Conversely, excessive laser power (>270 W) or a low scanning speed (<1.0 m/min) caused thermal decomposition of the CFRP due to its limited thermal resistance, leading to interfacial defects such as cracks and pores. The interface between the CFRP and TC4 coating primarily comprised granular TiC and acicular α' martensite, with minor TiS₂ detected. Optimal mechanical performance was achieved at a laser power of 250 W and a scanning speed of 1.2 m/min, yielding a maximum interfacial shear strength of 18.5 MPa. These findings provide critical insights for enhancing the load-bearing capacity of TC4/CFRP aeronautical composites, enabling their reliable operation in extreme aerospace environments.