Improving Tribological Performance of Poly(phenylene sulfide) by Incorporating PTFE Fillers: The Influence of Filler...

Poly(phenylene sulfide) (PPS) is a high-performance thermoplastic engineering material with excellent comprehensive performance that finds application in many fields due to its good processability, excellent heat resistance, and mechanical properties. However, the poor friction and wear properties of PPS limit its wide application in industrial sectors. In this work, polytetrafluoroethylene (PTFE) was adopted as the solid tribo-modifier to improve the tribological performance of PPS. The efficacy of using three types of PTFE fillers, namely PTFE fiber, micropowder, and nanopowder, was comparatively investigated. The results revealed that the incorporation of PTFE was beneficial to improving the tribological properties of PPS and PTFE nanopowders, which were prepared by irradiation treatment technology that demonstrated the best modification effect in terms of both tribological and mechanical performance among the studied systems. In addition, the coefficient of friction and specific wear rate of PPS composites with 30 wt% nanopowders reached 0.165 and 3.59 × 10^-5 mm³/Nm, respectively, which were 70.7% and 99.0% lower than their pure PPS counterparts. The above finding was attributed to the improved compatibility between the PTFE nanopowders and the PPS substrate as well as the easier formation of intact PTFE transfer film on the contact surface. This work shows some perspective for designing self-lubricating polymer composites that broaden their application in industrial sectors.