Comparative Study of Physicochemical Properties of Biochar Samples Derived from Nutshells as a Solid Fuel for Direct...

This paper presents the results of an investigation into the effect of the physicochemical properties of carbon chars (biochars) on the performance of direct carbon solid oxide fuel cells (DC-SOFCs). Biochars were obtained from walnut, coconut, pistachio, hazelnut and peanut shells by pyrolysis at a temperature of 850 °C. The results of structural studies conducted using X-ray diffraction and Raman spectroscopy reflected a low degree of graphitisation of carbon particles. Biochar derived from walnut shells is characterised by a relatively uniform content of alkali elements, such as sodium, potassium, calcium, magnesium and iron, which are natural components of the mineral residue and act as catalysts for the Boudouard reaction. This study of gasification of biochar samples in a CO₂ atmosphere recorded that the highest conversion rate from solid phase to gaseous phase was for the biochar sample produced from walnut shells. The superior properties of this sample are directly connected to structural features, as well as to the random distribution of alkali elements. DC-SOFCs involving 10 mol% of Sc₂O₃, 1 mol% of CeO₂, 89 mol% of ZrO₂ (10S1CeZ) or 8 mol% of Y₂O₃ in ZrO₂ (8YSZ) were used as both solid oxide electrolytes and components of the anode electrode. It was found that the highest electrochemical power output (P_max) was achieved for DC-SOFCs fuelled by biochar from walnut shells, with around 103 mW/cm² obtained for such DC-SOFCs involving 10S1CeZ electrolytes.