Edgewise Compressive Properties of Ecological Sandwich Panels with Engineered Bamboo Face Sheets and Bamboo Culm Core

Bamboo is a green, renewable material with high strength and low cost, but raw bamboo has limited application in residential buildings due to its irregular shape and dry cracking. In this regard, this work proposed a novel ecological sandwich panel to explore the potential combination of engineered bamboo and raw bamboo culms. Face sheets made of glued laminated bamboo panels were bonded to the bamboo culm core via epoxy resin and mortise-tenon joints. Two groups of specimens with height-to-thickness ratios of 4.63 and 5.37 were tested through edgewise compression to investigate the failure modes, strength and rigidity. The results revealed that the specimens had no overall stability problem under axial loading, but exhibited delamination and local bulging to the face sheets. When the height-to-thickness ratio increased from 4.63 to 5.37, but still belonged to the short member range, the area of the adhesive interface increased by 16.13%, and the edgewise compressive strength and rigidity increased by 17.57% and 35.04%, respectively. This indicated that the capacity and rigidity were mainly determined by the connection strength, which was obviously affected by the manufacturing and assembly errors. Accordingly, increasing the connection strength could be helpful for improving the load-carrying capacity and ductility of such panels.