High-Sensitivity, Low-Hysteresis, Flexible Humidity Sensors Based on Carboxyl-Functionalized Reduced-Graphene...

The measurement of humidity is of great significance for precision instruments, semiconductor integrated circuits, and element manufacturing factories. The oxygen-containing groups and noble metals in graphene-based sensing materials can significantly influence their humidity-sensing performance. Herein, 1,3,5-benzenetricarboxylic acid-functionalized reduced graphene oxide (H3BTC-rGO) loaded with Ag nanocluster nanocomposites (H3BTC-rGO/Ag) was synthesized via a facile one-step reduction method. The H3BTC-rGO/Ag-based sensor exhibited excellent humidity-sensing performance, including a higher sensitivity of 88.9% and a faster response/recovery time of 9 s/16 s towards 50% RH than those of other GO-, rGO-, and H3BTC-rGO-based sensors. The proposed humidity sensor was tested in the range of 0% to 100% RH and showed excellent sensitivity even at a low relative humidity of 0-10% or a high relative humidity of 90-100%. In addition, the H3BTC-rGO/Ag-based sensor had excellent selectivity, reliable repeatability, and good stability over 30 days under different relative humidities. Compared with H3BTC-rGO-200, the H3BTC-rGO/Ag-0.25-based sensor exhibited a low hysteresis of less than ±5% RH. The high performance was ascribed to the high density of the carboxyl groups and good conductivity of H3BTC-rGO, as well as the catalytic role of the Ag nanoclusters, resulting in high water adsorption rates. The potential applications of the H3BTC-rGO/Ag-based humidity sensor in human exhalation monitoring are also discussed. This work provides a reference for the application of graphene-based flexible sensors in monitoring very wet and dry environments.