Influence of Grinding Parameters on Surface Roughness and Subsurface Crack Damage Depth of Sapphire Crystal

Single sapphire crystals has been widely used in technology such as light emitting diodes, lasers, high-temperature and high-voltage devices, special windows, and optical systems, and grinding is an important process of their machining. In order to reveal the influence of the grinding wheel speed, grinding depth, and feed rate on the ground surface quality of sapphire crystals, a three-factor and five-level orthogonal experiment was designed and completed. Variance and range analysis was conducted on the experimental results using the surface roughness Ra and subsurface crack damage depth (SSD) as evaluation indicators, and optimized parameter combinations were explored. Furthermore, mathematical prediction models for the power regression of the Ra and SSD were established based on the experimental data. The research results indicate that within the range of the process parameters used in this experiment, the grinding process did not achieve the full ductile removal of the material. Some of the material was removed in a brittle mode, forming fractured pits on the ground surface, and median crack propagation occurred in the subsurface, forming a subsurface microcrack damage layer. The influence of the grinding parameters on the Ra and SSD showed a consistent trend, which was that the parameter with the greatest impact was the grinding wheel speed, followed by the feed rate and grinding depth. The Ra and SSD obtained under the optimized grinding parameter combination were 0.326 μm and 2.86 μm, respectively. The research results provide an experimental basis and guidance for improving the surface quality of sapphire crystals during grinding.