Tensile Behavior and Failure Mechanism of Bamboo Fiber Bundle and Its Scrimber Under Different Strain Rates

In this study, bamboo fiber bundles were directly extracted from raw bamboo material to fabricate reconstituted bamboo using the traditional hot-pressing method. The tensile behaviors and failure mechanisms of both the bamboo fiber bundle and its bamboo scrimber under various strain rates (quasi-static, 350/s, 950/s and 1700/s) were investigated by the SHTB system (split-Hopkinson tensile bar, high-speed camera and digital image correlation method). The results showed that the bamboo scrimber exhibited an obvious positive strain rate effect. The ultimate tensile strength of the bamboo scrimber at a strain rate of 1700/s was close to 200 MPa, but it was only about 80 MPa under quasi-static loading. This experimental result was further validated by the tensile behaviors of single bamboo fiber bundles at different strain rates (quasi-static, 300/s, 700/s and 1500/s). In addition, as the strain rate increased, the fracture surface of the bamboo changed from a linear shape to a discontinuous folded shape.