Mechanical Properties and Failure Mechanism of Recycled Concrete with Different Coal Gangue Powder Contents

In this study, the mechanical properties and failure characteristics of concrete with 10-20 mm recycled coarse aggregate at 0%, 25%, 50%, 75%, and 100% substitution rates were studied. In addition, the influence of coal gangue powder (CGP) on the mechanical properties of concrete was studied under the dosages of 5%, 10%, 15%, and 20%. The research results show that the peak strength of recycled concrete decreases with the increase in the replacement rate of 10-20 mm recycled coarse aggregate. When the replacement rate is 25%, the decrease in strength is the smallest. When the content of CGP increases from 0 to 20%, the peak strength of recycled concrete increases first and then decreases. When the content of CGP is 15%, the peak strength reaches the maximum value. The peak strength increases slightly. The density of pores and cracks in recycled concrete increases with the increase of 10-20 mm recycled coarse aggregate replacement rate. When the substitution rate exceeds 25%, the proportion of cracks increases by nearly 1.7 times. After adding CGP to recycled concrete, the pore density and crack ratio inside a specimen are significantly reduced. When the CGP content exceeds 15%, the crack ratio tends to be stable. When the CGP content is 15%, the crack ratio is 0.519%, which is 23.5% lower than that of the RAC-25 specimen. When the content exceeds 15%, the crack ratio tends to be stable.