Phase-field study of the effective fracture energy increase during dynamic crack propagation in disordered...

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...

As discussed in previous lessons, strain energy in a material is the energy stored when it is elastically deformed, a concept crucial in materials science and mechanical engineering. This energy results from the internal work done against the cohesive forces within the material. When a material undergoes shearing stress and corresponding shearing strain, the strain energy density, which is the energy stored per unit volume, is calculated. Within the elastic limit, where the stress is...

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...

The stress-strain relationship in ductile materials such as structural steel or aluminium is intricate and progresses through several stages. When a specimen is loaded, it initially exhibits a linear length increase, depicted by a steep straight line on the stress-strain diagram. It indicates the material is elastically deforming and will return to its original shape once unloaded. However, when a critical stress value is reached, plastic deformation begins. This stage sees substantial...

A material's elastic behavior is characterized by the disappearance of stress once the load is removed, allowing the material to return to its original state. However, when stress surpasses the yield point, yielding commences, marking the onset of plastic deformation or permanent set. This change from elastic to plastic behavior is influenced by the peak stress value and the duration before the load is removed. An intriguing observation occurs when a specimen is loaded, unloaded, and...

Understanding the strain energy density in materials under axial load is crucial for evaluating their mechanical behavior and durability. When a rod is subjected to such a load, it elongates and stores energy, known as strain energy, as potential energy within the material. This energy is measured in terms of energy per unit volume.
In the elastic region of a material, the relationship between the stress and the strain is linear and follows Hooke's Law. The strain energy density in this...