Evaluation of Two Alloplastic Biomaterials in a Critical-Size Rat Calvarial Defect Model

to evaluate the bone regeneration capacity of two alloplastic biomaterials in a critical-size rat calvarial defect model.

A total of 80 rats were randomized into 8 groups of 10 animals each. An Ø8 mm, critical-size calvarial defect was created, and the following treatments were randomly allocated: sham surgery, deproteinized bovine bone mineral (DBBM) + collagen membrane (CM), poly-(lactic-co-glycolic-acid) (PLGA)-coated pure phase β-tricalcium phosphate (β-TCP), or PLGA-coated 60% hydroxyapatite (HA):40%β-TCP. Animals were allowed to heal for 2 and 6 weeks. Microcomputed tomography (μCT) was used to evaluate mineralized tissue and biomaterial displacement. Histological samples were used to evaluate new bone formation.

μCT analysis showed no significant differences among groups for total volume of mineralized tissue or residual biomaterials. DBBM + CM showed significantly increased horizontal biomaterial displacement at 2 weeks but not at 6 weeks. Histological analysis showed that sham surgery had a significantly higher percentage of bone area fraction than the DBBM + CM and PLGA + β-TCP at 2 weeks, but not at 6 weeks. Residual biomaterial area fraction showed no significant differences among experimental groups at any healing time.

The alloplastic biomaterials showed suitable construct integrity and retention in the defect. All biomaterials were associated with limited new bone formation comparable to the sham surgery control.