Nucleation-promoting and growth-limiting synthesis of disordered rock-salt Li-ion cathode materials

Disordered rock-salt oxides and oxyfluorides are promising positive electrode materials for high-performance lithium-ion batteries free of nickel and cobalt. However, conventional synthesis methods rely on post-synthesis pulverization to achieve cycling-appropriate particle sizes, offering limited control over particle microstructure and crystallinity. This accelerates degradation and complicates secondary particle processing. Here we present a synthesis strategy that enhances nucleation while suppressing particle growth and agglomeration across various disordered rock-salt compositions, including lithium-manganese-titanium oxide, lithium-manganese-niobium oxide, and lithium-nickel-titanium oxide systems. Applied to Li_1.2Mn_0.4Ti_0.4O₂, this method yields highly crystalline, well-dispersed sub-200 nm particles that form homogeneous electrode films with stable cycling behavior. Tested in cells with lithium metal as the counter electrode, these electrodes deliver ~200 mAh/g with 85% capacity retention relative to the first cycle after 100 cycles (20 mA/g, 1.5-4.8 V), and an average discharge voltage loss of 4.8 mV per cycle, compared to 38.6% retention and 7.5 mV loss per cycle for electrodes derived from pulverized solid-state particles. This approach suggests a route to enhance the performance and durability of disordered rock-salt electrodes for sustainable lithium-ion batteries.