Repeated Impact Damage Behavior and Damage Tolerance of Bio-Inspired Helical-Structured Glass Fiber Resin Matrix

Liang He1, Zhaoyue Yao1, Lanlan Jiang1

  • 1School of Science, Harbin Institute of Technology, Shenzhen 518055, China.

Polymers
|July 12, 2025
PubMed

Keywords:
damage tolerancefinite element analysisimpact behaviorresin matrix composites

More Related Videos

A Testing Platform for Durability Studies of Polymers and Fiber-reinforced Polymer Composites under Concurrent Hygrothermo-mechanical Stimuli07:15

A Testing Platform for Durability Studies of Polymers and Fiber-reinforced Polymer Composites under Concurrent Hygrothermo-mechanical Stimuli

Published on: December 11, 2014

13.9K
Cutting Procedures, Tensile Testing, and Ageing of Flexible Unidirectional Composite Laminates07:53

Cutting Procedures, Tensile Testing, and Ageing of Flexible Unidirectional Composite Laminates

Published on: April 27, 2019

8.4K

Related Concept Videos

Fiber Reinforced Concrete01:22

Fiber Reinforced Concrete

Fiber-reinforced concrete significantly enhances the structural and nonstructural properties of traditional concrete by incorporating fibers like steel, glass, and polymers. These fibers, varying from natural ones such as sisal and cellulose to manufactured ones like polypropylene and Kevlar, are mixed into hydraulic cement with aggregates. Steel fibers, often preferred for their robustness, contribute to improved ductility, toughness, and post-cracking performance. The concrete is classified...
142
Plastic Behavior01:21

Plastic Behavior

A material's elastic behavior is characterized by the disappearance of stress once the load is removed, allowing the material to return to its original state. However, when stress surpasses the yield point, yielding commences, marking the onset of plastic deformation or permanent set. This change from elastic to plastic behavior is influenced by the peak stress value and the duration before the load is removed. An intriguing observation occurs when a specimen is loaded, unloaded, and...
268
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
243
Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
2.8K
Plastic Deformations01:19

Plastic Deformations

Plastic deformation represents a fundamental concept in materials science, which explains the irreversible change in the shape of a material when it experiences stress beyond its elastic capability. This phenomenon is important in structural engineering, especially in designing and analyzing cantilever beams—structures that are securely fixed at one end and bear loads at the opposite end. When these beams are subjected to loads within their elastic range, they will return to their...
188