Atomistic Observation of Defect Generation and Microstructural Evolution in Polycrystalline FeCrAl Alloys Under...

FeCrAl alloys have garnered considerable attention as candidate cladding materials for light water reactors due to their promising mechanical stability and irradiation resistance. However, the response characteristics of these alloys to irradiation and the associated mechanisms remain poorly understood. This study provides atomistic insights into irradiation-induced defect formation and microstructural evolution in polycrystalline FeCrAl. Using the LAMMPS molecular dynamics code, displacement cascades were simulated under irradiation doses ranging from 0.05 dpa to 0.5 dpa while evaluating the dependencies on temperature and grain size. The interaction between pre-existing defects and irradiation-induced microstructures (point defects, dislocations, clusters, etc.) was visualized and analyzed visually and quantitatively. The results indicate that the irradiation dose increases the number of surviving Frenkel pairs, whereas elevated temperatures reduce their stability. The cluster fraction of interstitials increases with both irradiation dose and temperature, while that of vacancies decreases at higher temperatures due to their lower stability. In the initial phase of the displacement cascade, the density and distribution of dislocations evolve continuously until the annealing stage. The dislocation density at the end of the annealing phase decreases with increasing dose and temperature. The thickness of grain boundaries increases with the irradiation dose, and the regions adjacent to grain boundaries transform into an amorphous state at higher dose levels. As both the irradiation dose and temperature increase, the amorphization process accelerates, and smaller grain size leads to a greater degree of amorphization.