The Design of the Ni₃N/Nb₄N₅ Heterostructure as Bifunctional Adsorption/Electrocatalytic Materials for Lithium-Sulfur...

Lithium-sulfur (Li-S) batteries are hindered by the sluggish electrochemical kinetics and poor reversibility of lithium polysulfides (LiPSs), which limits their practical energy density and cycle life. In order to address this issue, a novel Ni₃N/Nb₄N₅ heterostructure was synthesized via electrospinning and nitridation as a functional coating for polypropylene (PP) separators. Adsorption experiments were conducted in order to ascertain the heterostructure's superior affinity for LiPSs, thereby effectively mitigating their shuttling. Studies of Li₂S nucleation demonstrated the catalytic role of the substance in accelerating the deposition kinetics of Li₂S. Consequently, Li-S cells that employed the Ni₃N/Nb₄N₅-modified separator were found to achieve significantly enhanced electrochemical performance, with the cells delivering an initial discharge capacity of 1294.4 mAh g^-1 at 0.2 C. The results demonstrate that, after 150 cycles, the cells retained a discharge capacity of 796.2 mAh g^-1, corresponding to a low capacity decay rate of only 0.25% per cycle. In addition, the rate capability of the cells was found to be improved in comparison to control cells with NiNb₂O₆-modified or pristine separators.