Enhancing the Performance of LLO Through Vanadium Doping and Abundant Exposed (010) Planes in Secondary Particles

Lithium-rich layered oxide (LLO) has received extensive attention from researchers due to its high initial discharge capacity (≥250 mAh g^-1). However, defects such as its high initial irreversible capacity, voltage decay, and poor rate performance have severely limited its commercialization. These issues arise because the Li₂MnO₃ component in LLO is activated during the initial cycle, leading to the participation of lattice oxygen anions (O^2-) in redox reactions. This results in irreversible oxygen loss (O₂) and subsequent structural phase transitions. To address these challenges, this study focuses on Li₁.₂Ni₀.₁₃Co₀.₁₃Mn₀.₅₄O₂ as the host material, utilizing abundant exposed (010) plane secondary particles and employing a vanadium (V) doping strategy to enhance electrochemical performance. The V forms strong V-O bonds with the lattice oxygen, effectively suppressing irreversible oxygen loss and improving structural stability. The results demonstrate that the LLO achieves the best electrochemical performance as the doping amount is 1 mol%, and the capacity retention improves from 74.5% (undoped) to 86% (V-doped) after 140 cycles at 0.5 C.