Thermal Interaction Mechanisms of Ammonium Perchlorate and Ammonia Borane

Ammonia borane (AB), with a theoretical hydrogen content of 19.6 wt%, is constrained by its low crystalline density (0.758 g/cm³) and poor thermal stability (decomposing at 100 °C). In this study, AB/ammonium perchlorate (AP) composites were synthesized via freeze-drying at a 1:1 molar ratio. The integration of AP introduced intermolecular interactions that suppressed AB decomposition, increasing the onset temperature by 80 °C. Subsequent vacuum calcination at 100 °C for 2 h formed oxygen/fuel-integrated ammonium perchlorate borane (APB), which achieved decomposition temperatures exceeding 350 °C. The proposed mechanism involved AB decomposing into borazine and BN polymers at 100 °C, which then NH₃BH₂⁺/ClO₄^- combined to form APB. At 350 °C, APB underwent the following redox reactions: 4NH₃BH₂ClO₄ → N₂↑ + 4HCl↑ + 2B₂O₃ + N₂O↑ + O₂↑ + 7H₂O↑ + H₂↑, while residual AP decomposed. The composite exhibited improved density (1.66 g/cm³) and generated H₂, N₂, O_2, and HCl, demonstrating potential for hydrogen storage. Additionally, safety was enhanced by the suppression of AB's exothermic decomposition (100-200 °C). APB, with its high energy density and thermal stability, was identified as a promising high-energy additive for high-burning-rate propellants.