Induction of Strong Magneto-Optical Effect and High Compatibility with Si of BiFeO₃ Thin Film by Sr and Ti Co-Doping

The poor magnetic and magneto-optical properties of BiFeO₃, along with its significant lattice mismatch with silicon, have limited its application in silicon-based integrated magneto-optical devices. In this study, co-doping with Sr²⁺ and Ti⁴⁺ ions effectively transformed the trigonal structure of BiFeO₃ into a cubic phase, thereby reducing the lattice mismatch with silicon to 2.8%. High-quality, highly oriented, silicon-based cubic Sr,Ti:BiFeO₃ thin films were successfully fabricated using radio frequency magnetron sputtering. Due to the induced lattice distortion, the characteristic periodic spiral spin antiferromagnetic structure of BiFeO₃ was suppressed, resulting in a significant enhancement of the saturation magnetization of cubic Bi_0.5Sr_0.5Fe_0.5Ti_0.5O₃ (48.0 emu/cm³), compared to that of pristine BiFeO₃ (5.0 emu/cm³). Furthermore, the incorporation of Sr²⁺ and Ti⁴⁺ ions eliminated the birefringence effect inherent in trigonal BiFeO₃, thereby inducing a pronounced magneto-optical effect in the cubic Sr,Ti:BiFeO₃ thin film. The magnetic circular dichroic ellipticity (ψ_F) of Bi_0.5Sr_0.5Fe_0.5Ti_0.5O₃ reached an impressive 2300 degrees/cm.