Corrosion Behaviors of Ni80A Alloy Valve in Marine Engine Within Ammonia-Rich Environment

Ammonia fuel is regarded as a promising zero-carbon alternative to diesel in next-generation marine engines. However, the high-temperature ammonia-rich environment poses significant corrosion challenges to hot-end components such as valves. This study investigates the corrosion behavior of Ni80A alloy marine valves under the coupled effects of a high temperature and ammonia atmosphere. Using computational fluid dynamics (CFD), the service temperature of the valve and the ammonia concentration distribution inside the engine cylinder were identified. High-temperature corrosion experiments were conducted with a custom-designed setup. Results show that corrosion kinetics accelerated markedly with temperature: the initial corrosion rate at 800 °C was four times that at 500 °C, and the maximum corrosion layer thickness reached 37 μm-double that at lower temperatures. Microstructural analysis revealed a transition from a dense, defect-free corrosion layer at 500 °C to a non-uniform layer with coarse CrN particles and aggregated nitrides at 800 °C. Notably, surface hardness increased at both temperatures, peaking at 590 HV at 500 °C, while matrix hardness at 800 °C declined due to γ' phase coarsening and grain growth. This work provides detailed insight into the temperature-dependent ammonia corrosion mechanisms of marine Ni-based alloy valves, offering essential data for material design and durability assessment in ammonia-fueled marine engines.