Failure Behavior of Damaged Reinforced Concrete Pipe Rehabilitated with Fiber-Reinforced Mortar Lining

The spray-applied pipe lining (SAPL) method, extensively employed in the trenchless rehabilitation of reinforced concrete pipes (RCPs) due to its operational versatility, remains constrained by an incomplete understanding of the failure behavior of rehabilitated pipelines, thereby impeding optimal design strategies. This study proposes an analytical approach to evaluate the structural performance of pipes with fiber-reinforced mortar lining, with a particular focus on interface failure and its consequences. Two RCPs with an inner diameter of 1000 mm, repaired with 34 mm and 45 mm centrifugally sprayed fiber-reinforced mortar liners, were subjected to three-edge-bearing (TEB) tests. The elastic limit loads of the two pipes were 57% and 39% of their pre-rehabilitation conditions, while the ultimate loads were 45% and 69%. A thicker liner exhibits a greater susceptibility to interface failure, leading to wider cracks around the elastic stage during loading. Once the interface failure occurs, load redistribution allows the liner to resist further cracking and sustain higher capacity, demonstrating enhanced bearing performance. Critical factors influencing the failure process were analyzed to inform design optimization, revealing that improving the interface takes precedence, followed by thickness design.