Composites with Flax and Hemp Fibers Obtained Using Osmotic Degumming, Water-Retting, and Dew-Retting Processes

This study presents the application of flax (Linum usitatissimum L.) and hemp (Cannabis sativa L.) fibers into composites with polyethylene matrices. The applied fibers were obtained using osmotic, water-retting, and dew-retting processes. The study determined the impact of the fiber extraction method on the properties of the composites obtained from natural filler and polyethylene matrix. These properties included color, tensile strength, thermal stability, adhesion of filler to the polymer, and flammability. It has been shown that the addition of flax and hemp fibers improves the mechanical properties of the composite compared to pure polymer. The tensile strength of the pure polymer samples was 24.64 MPa, while the tensile strength of composites reinforced with flax fibers ranged from 31.26 to 34.45 MPa, and those reinforced with hemp fibers ranged from 31.41 to 33.36 MPa. Studying the composites' flammability showed that filling them with osmotic degummed hemp fibers reduced the maximum heat release rate by over 34% for hemp compared to pure polymer. This research shows that the composites filled with flax and hemp fibers, regardless of extraction method, are characterized by reduced flammability and improved mechanical properties compared to the pure polyethylene samples.