Failure analysis of 3Cr oil pipe body fracture

Jinzhi Wang1, Yan Li2, Xianren Kuang3

  • 1Tubular Goods Research Institute, China National Petroleum Corporation & State Key Laboratory of Service Behavior and Structural Safety of Petroleum Pipe and Equipment Materials, Xi'an, 710077, China. swawjz@qq.com.

Scientific Reports
|July 17, 2025
PubMed

Keywords:
3CrOil tube breakRepaired tubeStress corrosion

More Related Videos

Ultrasonic Fatigue Testing in the Tension-Compression Mode06:54

Ultrasonic Fatigue Testing in the Tension-Compression Mode

Published on: March 7, 2018

10.8K
Predicting Catalyst Extrudate Breakage Based on the Modulus of Rupture09:53

Predicting Catalyst Extrudate Breakage Based on the Modulus of Rupture

Published on: May 13, 2018

8.4K

Related Concept Videos

Bending of Material: Problem Solving01:09

Bending of Material: Problem Solving

In this lesson, determine the ratio of the maximum bending moments applied to two metal pipes, given that both pipes can withstand a maximum stress of 100 MPa. Both pipes have an outer radius of 1.8 cm. Pipe A has an inner radius of 1.5 cm, and Pipe B has an inner radius of 1 cm. The ratio of the maximum bending moment applied to two metallic pipes, each with a different inner and outer radius, is determined by considering their dimensions. The inner radius of the first pipe is 1.5 cm, and for...
246
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
243
Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
2.8K
Major Losses in Pipes01:28

Major Losses in Pipes

When a fluid flows through a pipe, it experiences energy losses due to frictional resistance along the pipe walls, known as major losses. These energy losses result in a pressure drop, which varies based on the flow conditions — whether laminar or turbulent — and the specific physical properties of the fluid and pipe.
Fluid flow can be classified as laminar or turbulent, primarily based on the Reynolds number. This dimensionless number reflects the relative influence of inertial to...
1.3K
Single Pipe Systems01:24

Single Pipe Systems

In pipe flow analysis, problems are typically categorized into three types — Type I, Type II, and Type III — based on the known parameters and the desired outcome. Each type of problem addresses specific engineering requirements using fluid properties, pipe characteristics, and operational conditions.
In a Type I problem, fluid properties (density and viscosity), pipe characteristics (including diameter, length, and surface roughness), and the flow rate or average velocity are...
196
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
210