Polyaniline/Ti₃C₂ MXene Composites with Artificial 3D Biomimetic Surface Structure of Natural Macaw Feather Applied...

In this paper, a series of polyaniline (PANI)/Ti₃C₂ MXene composites (PMCs) with a biomimetic structure were prepared and employed as an anticorrosion coating application. First, the PANI was synthesized by oxidative polymerization with ammonium persulfate as the oxidant. Then, 2D Ti₃C₂ MXene nanosheets were prepared by treating the Ti₃AlC₂ using the optimized minimally intensive layer delamination (MILD) method, followed by characterization via XRD and SEM. Subsequently, the PMC was prepared by the oxidative polymerization of aniline monomers in the presence of Ti₃C₂ MXene nanosheets, followed by characterization via FTIR, XRD, SEM, TEM, CV, and UV-Visible. Eventually, the PMC coatings with the artificial biomimetic surface structure of a macaw feather were prepared by the nano-casting technique. The corrosion resistance of the PMC coatings, evaluated via Tafel polarization and Nyquist impedance measurements, shows that increasing the MXene loading up to 5 wt % shifts the corrosion potential (E_corr) on steel from -588 mV to -356 mV vs. SCE, reduces the corrosion current density (I_corr) from 1.09 µA/cm² to 0.035 µA/cm², and raises the impedance modulus at 0.01 Hz from 67 kΩ to 3794 kΩ. When structured with the hierarchical feather topography, the PMC coating (Bio-PA-MX-5) further advances the E_corr to +103.6 mV, lowers the I_corr to 7.22 × 10^-4 µA/cm², and boosts the impedance to 96,875 kΩ. Compared to neat coatings without biomimetic structuring, those with engineered biomimetic surfaces showed significantly improved corrosion protection performance. These enhancements arise from three synergistic mechanisms: (i) polyaniline's redox catalysis accelerates the formation of a dense passive oxide layer; (ii) MXene nanosheets create a tortuous gas barrier that cuts the oxygen permeability from 11.3 Barrer to 0.9 Barrer; and (iii) the biomimetic surface traps air pockets, raising the water contact angle from 87° to 135°. This integrated approach delivers one of the highest combined corrosion potentials and impedance values reported for thin-film coatings, pointing to a general strategy for durable steel protection.