An Experimental Investigation on the Flow Boiling Heat Transfer Performance of Nanofluid in 3D Printing Minichannel...

A minichannel heat sink combining flow boiling heat transfer with nanofluid is an ideal solution for the long-term cooling of high-power equipment. In the present paper, three mass fractions for 0.01 wt%, 0.05 wt%, and 0.1 wt% graphene/R141b and Al₂O₃/R141b nanofluids are prepared by ultrasonic vibration. The flow boiling heat transfer performance for graphene/R141b and Al₂O₃/R141b nanofluids was contrastively investigated in a 3D printing 10-minichannel heat sink with a single channel dimension of 198 mm × 1.5 mm × 1.5 mm. The results indicate that the heat transfer performance of graphene/R141b and Al₂O₃/R141b nanofluids are enhanced after adding nanoparticles in pure R141b, and the maximum average heat transfer coefficients of graphene/R141b and Al₂O₃/R141b nanofluids, respectively, increase by 35.4% and 31.7% compared with that of pure R141b. The heat transfer performance of graphene/R141b and Al₂O₃/R141b nanofluids increases nonlinearly with the increase in mass concentration; the heat transfer coefficient reaches its maximum at the mass concentration of 0.02 wt%, and then, it decreases slightly, which is mainly caused by nanoparticle deposition, leading to silted channel surface cavities during the flow boiling experiment. Moreover, it has been discovered that the heat transfer coefficient of graphene/R141b is larger than that of Al₂O₃/R141b under the same conditions. The average heat transfer coefficient of graphene/R141b increased by 19.7% compared with that of Al₂O₃/R141b. The main reason for this is that graphene nanosheets have a larger contact area with the liquid working medium compared with nanoparticle Al₂O₃, and the graphene/R141b thermal conductivity is also significantly higher than that of Al₂O₃/R141b nanofluids. The research results can provide a basis for the practical application of nanofluids in heat sinks.