Microstructure and Chemical Stability of Al₂O₃-ZrO₂-ReB₂ Composite Coatings Obtained by Air Plasma Spraying

This study investigated the effect of adding superhard ReB₂ to atmospheric plasma sprayed (APS) coatings based on 60 wt% Al₂O₃ and 40 wt% ZrO₂. The amorphous phases commonly present in such coatings are known to impair their performance. ReB₂ was introduced as a crystallization nucleus due to its high melting point. ReB₂ decomposes in the presence of moisture and oxygen into H₃BO₃, ReO₃, HBO₂, and HReO₄. ReB₂ was encapsulated with Al₂O₃ via metallothermic synthesis to improve moisture stability, yielding a powder with d₉₀ = 15.1 μm. After milling, it was added at 20 wt% to the Al₂O₃-ZrO₂ feedstock. Agglomeration parameters were optimized, and coatings were deposited under varying APS conditions onto 316L steel substrates with a NiAl bond coat. In the coating with the highest ReB₂ content, the identified phases included ReB₂ (2.6 wt%), Re (0.8 wt%), α-Al₂O₃ (30.9 wt%), η-Al₂O₃ (32.4 wt%), and monoclinic and tetragonal ZrO₂. The nanohardness of the coating, measured using a Vickers indenter at 96 mN and calculated via the Oliver-Pharr method, was 9.2 ± 1.0 GPa. High abrasion resistance was obtained for the coating with a higher content of η-Al₂O₃ (48.7 wt%). The coefficient of friction, determined using a ball-on-disc test with a corundum ball, was 0.798 ± 0.03. After 15 months, the formation of (H₃O)(ReO₄) was observed, suggesting initial moisture-induced changes. The results confirm that Al₂O₃-encapsulated ReB₂ can enhance phase stability and crystallinity in APS coatings.