The Improvement of Road Performance of Foam Asphalt Cold Recycled Mixture Based on Interface Modification

With the increasing demand for highway maintenance, enhancing the resource utilization of reclaimed asphalt pavement (RAP) has become an urgent and widely studied issue. Although foam asphalt cold recycling technology offers significant benefits in terms of resource utilization and energy saving, it still faces challenges, particularly the poor stability of foam asphalt mixtures. This study focuses on optimizing the performance of foam asphalt recycled mixtures through interface modification, aiming to promote the widespread application of foam asphalt cold recycling technology. Specifically, the research follows these steps: First, the optimal mix ratio of the recycled mixtures was determined based on the fundamental properties of foam asphalt and RAP. Then, zinc oxide, silane coupling agents, and amine anti-stripping agents were introduced to modify the recycled mixtures. At last, a series of tests were conducted to comprehensively evaluate improvements in road performance. The results indicate that the silane coupling agent enhances the low-temperature performance and fatigue. The fracture energy reached 526.71 J/m². Zinc oxide improves the low-temperature cracking resistance and dry shrinkage performance. Amine anti-stripping agents have minimal impact on the low-temperature performance. The linear shrinkage was reduced by 2.6%. The results of TOPSIS indicated that silane coupling agent modification exhibits superior fatigue resistance and low-temperature performance, achieving the highest comprehensive score of 0.666. Although amine-based anti-stripping agents improve fatigue life, they are not suitable for modifying foamed asphalt mixtures due to their detrimental effects on low-temperature performance and moisture resistance.